Properties | Unit | Test Method | Value | |
---|---|---|---|---|
PU307 | PT306 | |||
Total Thickness ( Tolerance: ±0.05% ) | mm | UPS method | 0.40 ~ 0.90 | |
Total Width | mm | Scale | Up to 1300 | |
Thermal Shrinkage (MD) | % | On solar glass (5 min, 25 ºC) | ≤ 3 | ≤ 3 |
Thermal Creep | mm | 90ºC, 250hrs | ≤ 1 | ≤ 1 |
Shore Hardness | Shore A | ASTM D 2240 | 70 ± 5 | 70 ± 5 |
Melting Point | ºC | ASTM D3417 | 70 ± 5 | 70 ± 5 |
Degree of Cross-linking (Gel Content) | % | Soxhlet Method Lamination (10 min,145 ºC) | ≥ 70 | ≥ 70 |
Adhesion to Glass (With Backsheet) | N/㎝ | ASTM D 903 | ≥ 60 | ≥ 60 |
Adhesion to Backsheet | N/㎝ | ASTM D 903 | ≥ 70 | ≥ 70 |
Ultimate Elongation (Cured) | % | ASTM D 638 | ≥ 600 | ≥ 600 |
Tensile Strength (Cured) | MPa | ASTM D 638 | 12 ± 3 | 12 ± 3 |
Optical Transmittance | % | ASTM E424 | ≥ 91 | ≥ 91 |
UV Cut-off Wave Length | nm | UPS Method | 360 | UV transparent |
Heat / Humidity Resistance (80ºC, 85%RH, 2000hrs) | ΔYI | ASTM E 313 | ≤ 5 | ≤ 5 |
Water Absorption (Cured) | % | ISO 62-200805 | ≤0.1 | ≤ 0.1 |
Volume Resistivity (Cured) | Ω*cm | ASTM D 257 | ≥ 1*1015 | ≥ 1*1015 |
N-Topcon Modülleri için
Solar Cam |
PT306 (POE) |
N-Topcon hücre |
EU307 (EVA) |
Backsheet |
Solar Cam |
EPET306 (EPE) |
N-Topcon hücre |
EU307 (EVA) |
Solar Cam |
P-PERC Bifacial Cam-Cam Modüller için
Solar Cam |
EPET306 (EPE) |
P-PERC Bifacial hücre |
EPET306 (EPE) |
Solar Cam |
Solar Cam |
ET306 (EVA) |
P-PERC Bifacial hücre |
PT306 (POE) |
Solar Cam |
Solar Cam |
ET306 (EVA) |
P-PERC Bifacial hücre |
EPET306 (EPE) |
Solar Cam |
P-PERC Bifacial Cam-Backsheet Modüller için
Solar Cam |
ET306 (EVA) |
P-PERC Bifacial hücre |
EU307 (EVA) |
Beyaz Backsheet |
Solar Cam |
ET306 (EVA) |
P-PERC Bifacial hücre |
EPEU307 (EPE) |
Şefaf Backsheet |
Solar Cam |
ET306 (EVA) |
P-PERC Bifacial hücre |
EU307 (EVA) or EPEU307 (EPE) |
Siyah Backsheet |